MXD6 materials MXD6 is a crystalline polyamide resin, which is synthesized by condensation of m-phenylenedimethylamine and adipic acid. 1、Maintain high strength and rigidity in a wide temperature range 2、High heat deflection temperature, small coefficient of thermal expansion 3、Low water absorption, small size change after water absorption, less mechanical strength reduction 4、Small shrinkage rate of molding, suitable for precision molding process 5、Excellent paintability, especially suitable for surface painting under high temperature 6、Excellent barrier to oxygen, carbon dioxide and other gases MXD6-LGF materials MXD6 can be laminated with glass and carbon fibers for materials containing 20-60% glass fiber reinforcement with exceptional strength and stiffness. Even when filled with high levels of glass fiber, its smooth, resin-rich surface creates a high gloss surface as without glass fiber, making it extremely suitable for painting, metal coating or generating naturally reflective shells. 1. High fluidity for thin wall It is a very high flowing resin that can easily fill thin walls as thin as 0.5 mm thick even with glass fiber content as high as 60%. 2. Excellent surface finish The resin-rich perfect surface has a highly polished appearance, even with a high glass fiber content. 3. Very high strength and stiffness With 50-60% glass fiber reinforcement, MXD6 has a tensile and flexural strength similar to many cast metals and alloys. 4. Good dimensional stability At ambient temperature, the coefficient of linear expansion (CLTE) of MXD6 glass fiber composites is similar to that of many cast metals and alloys. It is highly reproducible due to low shrinkage and the ability to maintain tight tolerances (length tolerances can be as low as ± 0.05% if properly formed). Datasheet for reference produce processing Extrusion mold Injection mold Frequently asked questions Q. Does long glass fiber and long carbon fiber injection have special requirements for injection molding machines and molds? A. There are certainly requirements. Especially from the product design structure, as well as the injection molding machine screw nozzle and mold structure injection molding process must consider the requirements of long fiber. Q. How to choose the requirement method and length of the material when using long fiber reinforced thermoplastic material? A. The selection of materials depend on the requirements of the products. It is necessary to  assess how much the content is enhanced and how much length is more appropriate, which are depending on the performance of the products. Q. Under what circumstances can long fiber replace short fiber? What are the common alternative materials? A. Traditional staple fiber materials can be replaced with long glass fiber and long carbon fiber LFT materials in the case of customers whose mechanical properties cannot be met or where higher metal substitutes are desired. For example, PP long glass fiber is often replacing nylon reinforced glass fiber, and nylon long glass fiber is replacing PPS series. We will offer you 1. LFT & LFRT material technical parameters and leading edge design 2. Mold front design and recommendations 3. Provide technical support such as inejction molding and extrusion molding Main products

MXD6-LGF MXD6 can be laminated with glass fibers, filled with 30-60% long glass fibers, and has exceptional strength and stiffness. What sets this material apart is that even when filled with high levels of glass fiber, its smooth, resin-rich surface creates a high-gloss surface like that without the glass fiber, making it ideal for painting, metal coating, or generating naturally reflective housings. Advantages 1.High fluidity for thin walls MXD6 is a very high fluidity resin, even in the glass fiber content of up to 60%, it can still easily fill the thickness of only 0.5 mm thin wall. 2.Excellent surface finish The perfect surface of the resin-rich resin has a highly polished appearance, even with a high glass fiber content. 3.High strength and stiffness         MXD6 add 30%-60% glass fiber reinforcement, its tensile and flexural strength is similar to many cast metals and alloys. 4.good dimensional stability At ambient temperature, the coefficient of linear expansion (CLTE) of MXD6 glass fiber composites is close to that of many cast metals and alloys. Reproducibility is excellent due to low shrinkage and the ability to maintain tight tolerances (if properly molded, length tolerances can be as low as ± 0.05%). Application Automotive Industry/Aerospace Aircraft/Construction Tools/Household Goods Other materials you may wonder                            PA6-LGF                                    PA66-LGF                                 PA12-LGF                                                                  Certification Quality Management System ISO9001/16949 Certification National Laboratory Accreditaion Certificate Modified Plastics Innovation Enterprise Honorary Certificate Heavy metal REACH & ROHS testing Welcome to contact us