Long Glass fiber Reinforced Polyamide nylon PA6

/Glass Fiber Reinforced Nylon 6 Resin Pellets High Strength

Categories

New Products

Glass Fiber Reinforced Nylon 6 Resin Pellets High Strength

When molding nylon 6, the material is sometimes injected with a specified amount of glass fibers (usually between 20% and 60%) to boost its tensile strength. Glass fibers improve stiffness. Moreover, since UV radiation can be harmful to nylon, a UV stabilizer is frequently added to the material before injection molding to decrease the possible degradation of the item with time.

item no.:
PA 6 GF
Payment:
Discussed
product origin:
China
Color:
Natural color or Customized
shipping port:
Xiamen
Lead Time：
2-10 workings days

inquiry now

Product Detail

PA 6 Long Glass Fiber Reinforced Composite

High Strength | High Stiffness | Heat Resistant | Dimensionally Stable

Download Product Brochure (PDF)

Key Properties

PA6 long glass fiber composite delivers outstanding strength, stiffness, heat resistance, and dimensional stability, making it ideal for demanding engineering applications. Below are the main mechanical and thermal characteristics:

Property	Typical Value	Test Method
Density	1.43 g/cm³	ASTM D-792
Tensile Strength	189 MPa	ISO：527
Notched Impact Strength	35 KJ/m2	ISO：180
Heat Deflection Temperature	209 °C	ISO 75-2
Flexural Modulus	9623 MPa	GB/T 9341
Molding Shrinkage	0.10 - 0.30 %	ASTM D-955

Technical Advantages

Superior Mechanical Strength High Stiffness and Rigidity

Excellent Heat Resistance Good Chemical Resistance

Outstanding Dimensional Stability Enhanced Wear and Fatigue Resistance

Applications
PA6 long glass fiber composites are extensively used in engineering applications where strength, stiffness, and heat resistance are critical. Main fields of application include:

Automotive: engine covers, intake manifolds, pedal systems, structural brackets.

Electrical & Electronics: connectors, switch housings, coil bobbins, battery components.

Industrial: gears, bearings, pump housings, power tool parts.

Consumer Goods: sports equipment, mechanical components, high-performance housings.

Processing Guidelines

PA6 long glass fiber reinforced composites can be processed using conventional thermoplastic equipment. Recommended parameters:

Drying: Not always necessary, but 80℃ for 2–4 hours recommended if moisture >0.2%.

Injection Temperature: 243–272℃ depending on part thickness.

Mold Temperature: 54–93℃ for optimal surface quality.

Screw Design: Use low-shear screws to avoid fiber breakage.

Additional Information

Packaging: 25kg/bag or jumbo bag

Processing Methods: Injection molding / extrusion

Storage: Keep dry, avoid direct sunlight

Shelf Life: 12 months under recommended storage conditions

Certifications

Contact us on WhatsApp

Click here to chat directly→Start Chat

Related Tags :

Next:
High Stifiness PA 6 Long Glass Fiber Plastic White or Black Color

Send a Message

If you have any problem when using the website or our products, please write down your comments or suggestions, we will answer your questions as soon as possible!Thank you for your attention!

Subject : Glass Fiber Reinforced Nylon 6 Resin Pellets High Strength

If you have questions or suggestions,please leave us a message,we will reply you as soon as we can!

related products

PA6 Nylon Long Glass fiber Reinforced Polyamide

PA6 Long Glass fiber Reinforced Polyamide (nylon) ，Long glass fiber reinforced PA6 composite material prepared by solution impregnation process.

PA6 Nylon Polyamide long Glass fiber Reinforced

PA6 Long Glass fiber Reinforced Polyamide (nylon) ，Long glass fiber reinforced PA6 composite material prepared by solution impregnation process.

Nylon Polyamide long Glass fiber Reinforced PA6

Nylon Polyamide long Glass fiber Reinforced PA6，Long glass fiber reinforced PA6 composite material prepared by solution impregnation process.

Nylon PA6 Polyamide Glass fiber Plastic materials

Nylon PA6 Polyamide Glass fiber Plastic materials Nylon PA6 Polyamide Glass fiber Plastic materials; Resin PA6 Nylon with glass fiber composite plastic materials

Polyamide Glass fiber Plastic materials Nylon PA6

Nylon PA6 Polyamide Glass fiber Plastic materials Nylon PA6 Polyamide Glass fiber Plastic materials; Resin PA6 Nylon with glass fiber composite plastic materials